| About |
|---|
| EVATANE® 33-45 PV is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. EVATANE® 33-45 PV is exclusively dedicated to photovoltaic encapsulant films applications. The high Vinyl Acetate content of EVATANE® 33-45 PV brings transparency, flexibility and softness. It exhibits high dimensional stability when used in cross-linked formulations.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good Dimensional Stability,Crosslinked,Random copolymer,Soft |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 38 to 48 | g/10min | ASTM D1238，ISO 1133 |
| Vinyl acetate content | 32.0 to 34.0 | wt% | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | < 40.0 | ℃ | ISO 306/A , ASTM D1525 2 |
| Melting temperature | 62.0 | ℃ | ISO 11357-3 |
| Ring and Ball Softening Point | 107 | ℃ | ASTM E28 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 63 | ASTM D2240 , ISO 868 | |
| tensile strength | |||
| fracture | 9.00 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 900 to 1100 | % | ASTM D638 , ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 3. NF EN 1238 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |