| About |
|---|
| EVATANE® 42-60 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE® 42-60 brings softness, flexibility, polarity and high solubility. EVATANE® 42-60 can be readily dissolved into various solvents and be used in inks or solvent-base adhesives formulations.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Random copolymer,Soft |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 65 to 85 | g/10min | ISO 1133 |
| 190℃，2.16kg | 65 to 85 | g/10min | ASTM D1238 |
| Vinyl acetate content | > 41.0 | wt% | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | < 40 | ISO 868 | |
| Shaw’s A | < 40 | ASTM D2240 | |
| tensile strength | |||
| fracture | 5.00 | MPa | ASTM D638 |
| fracture | 5.00 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 900 to 1100 | % | ASTM D638 |
| fracture | 900 to 1100 | % | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | < 40.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | < 40.0 | ℃ | ISO 306/A |
| Melting temperature | 52.0 | ℃ | ISO 11357-3 |
| Ring and Ball Softening Point | 95 | ℃ | ASTM E28 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 3. NF EN 1238 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |