| Evolue™ SP1071C is a Linear Low Density Polyethylene product. It can be processed by extrusion and is available in Asia Pacific, Europe, or North America. Typical application: Packaging. Characteristics include: Fast Molding Cycle Good Sealability&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Quick molding cycle,Low temperature heat sealing |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 10 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | > 1000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 无断裂 | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 87.0 | ℃ | ISO 306 |
| Melting temperature | 100 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 51 | ISO 868 | |
| tensile strength | |||
| fracture | > 15.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 500 | % | ISO 527-2 |
| Bending modulus | 150 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |