| EvoSource™ ABS 4535 A UL-HB recognized, easy flowing, post-consumer recycled acrylonitrile-butadiene-styrene copolymer for general use. Available in standard grey (reference 70/15) and standard black (reference 90/04).&&EvoSource™ ABS 4535 A UL-HB recognized, easy flowing, post-consumer recycled acrylonitrile-butadiene-styrene copolymer for general use. Available in standard grey (reference 70/15) and standard black (reference 90/04). Other colors may be available upon request.&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good liquidity,Copolymer,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | Internal Method |
| Melt Flow Rate | |||
| 220℃，10.0kg | 22 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 41.0 | MPa | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2250 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 90.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| High Arc Burning Index (HAI) (1.5 to 2.8 mm) | PLC 1 | UL 746 | |
| Hot wire ignition (HWI) (1.5 to 2.8 mm) | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50-2.80 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.10 | % | |
| Processing (melt) temperature | 210 to 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.10 | % | |
| Melt temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. ASTM D 3847 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |