| Exact 3024 is an ethylene-based butene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. It can be used for both monolayer and multilayer coextruded cast film applications requiring excellent heat sealing performance.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 4.5 | g/10min | ASTM D1238 | |
| thickness | 25.4 | g/min | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| film | 5.72 | MPa | ASTM D882 |
| tensile strength | |||
| film | 4.96 | MPa | ASTM D882 |
| tensile strength | |||
| Fracture, thin film | 47.5 | MPa | ASTM D882 |
| tensile strength | |||
| Fracture, thin film | 31.6 | MPa | ASTM D882 |
| 1% secant modulus | 85.5 | MPa | ASTM D882 |
| 1% secant modulus | 97.2 | MPa | ASTM D882 |
| Puncture energy | 4.58 | J | ExxonMobil Method |
| Drop hammer impact | 110 | g | ASTM D1709-A |
| Elongation at break of thin film | 560 | % | ASTM D882 |
| Elongation at break of thin film | 780 | % | ASTM D882 |
| tear strength | 1.97 | g/micron | ASTM D1922 |
| tear strength | 5.91 | g/micron | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 93 | ASTM D2457 | |
| Haze μ M | 0.8 | % | ASTM D1003 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 97.2 | ℃ | Internal Method |
| Vicat Softening Temp | |||
| 87.2 | ℃ | ASTM D1525 | |
| Crystallization temperature | 82 | ℃ | 测试方法 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Value reported is an estimate based on ExxonMobil’s correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |