| About |
|---|
| Exceed 1012MK resin is an ethylene 1-hexene copolymer. Films made from Exceed 1012MK have outstanding cold temperature toughness, impact strength and puncture. These superior strength properties, along with excellent heat sealing and hot tack performance, make this a very versatile packaging film resin. Exceed 1012MK is TNPP-free.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | mPE |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.912 | g/cm³ | ExxonMobil Method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, MD | 119 | MPa | |
| 1% secant, TD | 133 | MPa | |
| tensile strength | |||
| MD, yield | 7.03 | MPa | |
| TD, yield | 7.36 | MPa | |
| MD, fracture | 54.7 | MPa | |
| TD, fracture | 48.1 | MPa | |
| Tensile strain | |||
| MD, fracture | 460 | % | |
| TD, fracture | 580 | % | |
| Drop hammer impact | 500 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD | 210 | g | |
| TD | 330 | g |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 45 | ASTM D2457 | |
| Haze | 15 | % | ASTM D1003 |
| Legal Statement | Nominal value | Unit | Test method |
|---|---|---|---|
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |