| About |
|---|
| Exelene® HDPE 5502: Antioxidant Exelene® HDPE 5502AS: Antioxidant, Antistatic&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Inoxidizability,Copolymer,Antistatic property,Hexene copolymers |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.955 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.35 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 30 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 60 ℃, 10% wetting agent, F50 | > 500 | hr | ASTM D1693B |
| 50 ℃, 3.10 mm, 100% wetting agent, F50 | 45.0 | hr | ASTM D1693A |
| 50 ℃, 1.90 mm, 100% wetting agent, F50 | 35.0 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 270 | J/m | ASTM D256-A |
| Tensile impact strength | 242 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 76.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746A |
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 5 |
| Melting temperature | 129 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second, 23 ℃ | 67 | ASTM D2240 | |
| tensile strength | |||
| yield | 27.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 600 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 1380 | MPa | ASTM D790-B |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |