| Exelene® HDPE 6007是一种高密度聚乙烯产品,。 它可以通过挤出吹塑成型进行加工,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 Exelene® HDPE 6007的应用领域包括瓶子 和 食品接触应用。 特性包括: 均聚物 抗氧化剂 可接触食品&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Inoxidizability,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.964 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.65 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 50 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 3.10 mm, 100% wetting agent, F50 | 15.0 to 20.0 | hr | ASTM D1693A |
| 50 ℃, 1.90 mm, 100% wetting agent, F50 | 8.00 to 10.0 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | 126 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 79.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746A |
| Vicat Softening Temp | 130 | ℃ | ASTM D1525 6 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second, 23 ℃ | 65 | ASTM D2240 | |
| tensile strength | |||
| yield | 30.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 300 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 1650 | MPa | ASTM D790-B |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |