| About |
|---|
| High Heat Amorphous TPI Blend, Tg 267C, High Continuous Use Temperature (CUT), Excellent FR, OSU and LOI. Material is UL listed. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Resin is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited. Also UL rated 94V0 at 1.3mm and 3.0mm.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | TPI |
| Material Status | Commercial: Negative |
| Features | Halogen free,Flame Characteristics,High Heat Resistance,Amorphous,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 6.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.0 to 1.2 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.60 | % | ASTM D570 |
| Saturation, 23 ℃ | 2.3 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 3420 | MPa | ASTM D638 |
| — | 3160 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 103 | MPa | ASTM D638 |
| yield | 101 | MPa | ISO 527-2/5 |
| fracture | 96.0 | MPa | ASTM D638 |
| fracture | 70.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 7.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/5 |
| fracture | 15 | % | ASTM D638 |
| fracture | 6.0 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 3130 | MPa | ASTM D790 |
| — | 2850 | MPa | ISO 178 |
| bending strength | |||
| — | 150 | MPa | ISO 178 |
| Yield, 50 mm span | 168 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 21 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 43 | J/m | ASTM D256 |
| 23℃ | 4.4 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 20.7 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 250 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 235 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 237 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 225 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 260 | ℃ | ASTM D1525 12 |
| B50 | 253 | ℃ | ISO 306 |
| B120 | 252 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~150℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：23~150℃ | 5.1E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 175 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |