| About |
|---|
| EXTRON 3007 FC is a 30% glass fibre reinforced polypropylene compound. It is a medium flow injection moulding grade developed for components requiring a combination of high rigidity, low shrinkage and improved creep resistance. It has been manufactured in accordance with Australian Standard AS 2070-1999 “Plastic Material for Food Contact Use”. The ingredients used in this formulation are referenced in the US Code of Federal Regulations, Volume 21, parts 170-199.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low contractility,Food contact compliance,Moderate liquidity |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.20 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3mm | 34 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3 mm | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.0 mm | 155 | ℃ | |
| 1.8 MPa, unannealed, 3.00 mm | 135 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃，3.00 mm | 3.0E-5 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3.00 mm | 80 | ||
| Shore D, 15 seconds, 3.00 mm | 75 | ||
| Rockwell hardness | |||
| R-grade, 3.00 mm | 113 | ASTM D785 | |
| tensile strength | |||
| 3 mm | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3 mm | 2.0 | % | ASTM D638 |
| Bending modulus | |||
| 3 mm | 6100 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Proposed maximum recycled material ratio | 10 | % | |
| Processing (melt) temperature | 200 to 260 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Injection speed | 中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |