| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | High crystallization,Quick molding cycle,High liquidity,Good Rigidity,Excellent Processability |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 30 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 2.9 | kJ/m² | ISO 179/1eA |
| -20℃ | 4.3 | kJ/m² | ISO 179/1eA |
| 0℃ | 5.2 | kJ/m² | ISO 179/1eA |
| 23℃ | 8.4 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -18℃ | 37 | J/m | ASTM D256-A |
| 23℃ | 85 | J/m | ASTM D256-A |
| -40℃ | 5.2 | kJ/m² | ISO 180-1A |
| -20℃ | 5.7 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Drop hammer impact | |||
| -29℃，3.18 mm | 14.5 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| DTUL, unannealed | 106 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 95 | ℃ | ISO 75-2/Bf |
| DTUL, Annealed | 117 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 54 | ℃ | ISO 75-2/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 94 | ASTM D785 | |
| Tensile modulus | 1440 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 25.8 | MPa | ASTM D638 |
| yield | 25.7 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.1 | % | ASTM D638 |
| yield | 4.8 | % | ISO 527-2/50 |
| Bending modulus | |||
| 1% secant, 0.051 in/min (1.3 mm/min) | 1380 | MPa | ASTM D790-A |
| 1% secant, 0.51 in/min (13 mm/min) | 1580 | MPa | ASTM D790-B |
| (0.079 in/min (2.0 mm/min) | 1380 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |