| HTA 108 is a homopolymer HDPE film grade designed to improve stiffness and barrier in coextrusion or in PE blends. When blended with LLDPE or metallocene LLDPE, HTA 108 improves their processability.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Ultra-high molecular weight polyethylene |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | ASTM D1238 | ||
| 46 | g/10min | ASTM D1238 | |
| 190℃，2.16kg | 0.70 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, TD | 1700 | MPa | ASTM D882 |
| 1% secant, MD | 1200 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture | 31.0 | MPa | ASTM D882 |
| MD, fracture | 60.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture | 2.0 | % | ASTM D882 |
| MD, fracture | 510 | % | ASTM D882 |
| Drop hammer impact | < 30 | g | ASTM D1709-A |
| Elmandorf tear strength | |||
| MD | 10 | g | ASTM D1922 |
| tear strength | |||
| TD | 200 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |