| About |
|---|
| HYA 600 is a general purpose HDPE resin, characterized by very easy processability, an excellent balance of rigidity and impact strength and a good ESCR.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Ultra-high molecular weight polyethylene |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.35 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 29 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 10% non-ionic detergent | < 20.0 | hr | ASTM D1693 |
| 100% non-ionic detergent | < 50.0 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 62 | ASTM D2240 | |
| Tensile modulus | 1100 | MPa | ASTM D638 |
| Tensile Strength（100% Strain） | 14.0 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 9.9 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |