| 一种均聚物树脂，用于需要优异流动性能和良好机械性能的注塑成型场合。它适用于瓶盖、瓶塞和一般用途的应用领域，例如玩具、电器、包装和薄壁部件。&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.3 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 79.0 | ℃ | ISO 75-2/B |
| Melting peak temperature | 159 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 70 | ISO 868 | |
| Tensile modulus | 1420 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 33.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 9.0 | % | ISO 527-2/1A/50 |
| Bending modulus | 1330 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |