| About |
|---|
| A medium flow homopolymer resin designed for mono-oriented products like stretched tapes and monofilament.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Gauge Control,Moderate liquidity,Low water portability |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | J/m | ASTM D256-A |
| Drop hammer impact | |||
| 23℃，3.2 mm | 3.04 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 93.5 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 106 | ASTM D785 | |
| tensile strength | |||
| yield | 35.1 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 9.8 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1480 | MPa | ASTM D790-A |
| 1% secant | 1700 | MPa | ASTM D790-B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 4. 0.51 in/min |
| 5. Geometry GC |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |