| About |
|---|
| 一种适用于挤出场合的抗冲击共聚物树脂，它具有高熔融粘度和优异的低温抗冲击强度。它适用于电缆、管道、型材、片材和热成型。&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Low liquidity,High impact resistance |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 230℃，2.16kg | 1.2 | g/10min | ISO 1133 |
| 230℃，5.0kg | 4.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ISO 868 | |
| Tensile modulus | |||
| Secant | 1270 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 26.9 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2/50 |
| Bending modulus | |||
| Secant | 1240 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20 ℃, completely fractured | 3.8 | kJ/m² | ISO 179 |
| 0 ℃, completely fractured | 5.4 | kJ/m² | ISO 179 |
| 23 ℃, localized fracture | 29 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23 ℃, localized fracture | 32 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.2 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 79.6 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 152 | ℃ | ISO 306/A50 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |