| About |
|---|
| A high crystallinity, high impact copolymer resin with medium melt flow rate and excellent processing attributes. It is designed for injection molded small and large appliance parts.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Nucleation,Quick molding cycle,Antistatic property,Rigid-tough balance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1320 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 24.4 | MPa | ASTM D638 |
| yield | 24.3 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.4 | % | ISO 527-2/50 |
| yield | 4.4 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1290 | MPa | ASTM D790-A |
| 1% secant | 1480 | MPa | ASTM D790-B |
| Bending modulus | 1250 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.9 | kJ/m² | ISO 179/1eA |
| -20℃ | 4.8 | kJ/m² | ISO 179/1eA |
| 0℃ | 6.6 | kJ/m² | ISO 179/1eA |
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 150 | J/m | ASTM D256-A |
| -40℃ | 4.0 | kJ/m² | ISO 180-1A |
| -18℃ | 4.6 | kJ/m² | ISO 180-1A |
| 23℃ | 8.4 | kJ/m² | ISO 180-1A |
| Drop hammer impact | |||
| -29℃，3.18 mm | 22.7 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 51.5 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 105 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 93.0 | ℃ | ISO 75-2/Bf |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 4. 0.51 in/min |
| 5. 0.079 in/min |
| 6. Geometry GC |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |