| About |
|---|
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Nucleation,High liquidity,High rigidity |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 60 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm³ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| 51 mm/min | 32.9 | MPa | ASTM D638 |
| 30.4 | MPa | ISO 527-2 | |
| Tensile Elongation | |||
| 51 mm/min | 5.0 | % | ASTM D638 |
| Tensile Strain | 4.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| 1.3 mm/min | 1650 | MPa | ASTM D790 |
| 1.3 mm/min | 1870 | MPa | ASTM D790 |
| 2.0 mm/min | 1660 | MPa | ISO 178 |
| Rockwell hardness | 101 | ASTM D-785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| -18℃ | 22 | J/m | ASTM D256 |
| 23℃ | 44 | J/m | ASTM D256 |
| -20℃ | 2.6 | KJ/m² | ISO 180/1A |
| 0℃ | 3.8 | KJ/m² | ISO 180/1A |
| 23℃ | 5.6 | KJ/m² | ISO 180/1A |
| Charpy Notched Impact Strength | |||
| -20℃ | 2.6 | kJ/m² | ISO 179/1eA |
| 0℃ | 3.8 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.3 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.80 MPa, unannealed | 55.5 | ℃ | ISO 75-1/-2 |
| 0.45 MPa, unannealed | 108 | ℃ | ISO 75-1/-2 |
| 0.45 MPa, unannealed | 121 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 127 | ℃ | ASTM D648 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |