| 一种特种热塑聚烯烃树脂，用于需要良好表面光洁度、高耐刮擦性和良好抗紫外线性能的汽车内饰。&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good liquidity,High scratch resistance |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 18 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 20.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| Secant, 23 ℃ | 2200 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 25.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23 ℃, completely fractured | 10 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23 ℃, completely fractured | 8.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 54.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 105 | ℃ | ISO 75-2/B |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |