| Ming Dih EPS LS3是一种发泡聚苯乙烯产品,。 它,在亚太地区有供货。 Ming Dih EPS LS3的应用领域包括安全设备 和 包装。&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 38 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 52.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| Secant | 1100 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 17.0 | MPa | ISO 527-2/50 |
| yield | 23.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 22 | % | ISO 527-2/50 |
| yield | 5.0 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| 0 ℃, completely fractured | 5.5 | kJ/m² | ISO 179 |
| 23 ℃, completely fractured | 9.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 51.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 82.0 | ℃ | ISO 75-2/B |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |