| Ferro PP MPP40FJ15NA is a Polypropylene Homopolymer (PP Homopolymer) product filled with 41% mica. It can be processed by injection molding and is available in Latin America or North America. Typical application: Appliances. Characteristics include: Chemically Coupled Creep Resistant Good Dimensional Stability Homopolymer&& |
| Product Description | |
|---|---|
| Supplier | Ferro |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good Dimensional Stability,Chemical coupling,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 13 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.90 | % | |
| TD | 1.1 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 27 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 150 | J/m | ASTM D4812 |
| Drop hammer impact | |||
| 23℃ | 0.452 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 138 | ℃ | |
| 1.8 MPa, unannealed | 85.0 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 82 | ASTM D2240 | |
| tensile strength | |||
| 23℃ | 33.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 10 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 1% secant, 23 ℃ | 3580 | MPa | |
| Tangent, 23 ℃ | 5140 | MPa | |
| bending strength | |||
| 23℃ | 53.8 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93.3 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 204 to 213 | °C | |
| Barrel middle temperature | 210 to 216 | °C | |
| Barrel front temperature | 216 to 218 | °C | |
| Nozzle temperature | 218 to 227 | °C | |
| Mold temperature | 43.3 to 57.2 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |