| DESCRIPTION: Random copolymer for injection molding. FEATURES: Clarified and antistatic agent. Produced without animal derived components. APPLICATIONS: Lab ware, food packaging.&& |
| Product Description | |
|---|---|
| Supplier | INVISTA |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Clarity,Random copolymer,ADCF,Antistatic property |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 23℃ | > 36.2 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.0 | ℃ | ASTM D648 |
| Melting peak temperature | 145 to 152 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 635 µm | 6.4 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 28.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 9.0 | % | ASTM D638 |
| Bending modulus | |||
| tangent | 1140 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 90 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |