Fibremod™ GB306SAF

About
Fibremod GB306SAF is a 35 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in standard black 9502. This material shows excellent mechanical properties also at elevated temperatures. Applications: Fibremod GB306SAF has been developed especially for demanding applications in under the bonnet applications. Air intake manifolds Parts for cooling systems Fans and shrouds Technical components exposed to high heat and laods Features: Long term high heat stabilized Copper (CU) stabilized&&

About

Fibremod GB306SAF is a 35 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in standard black 9502. This material shows excellent mechanical properties also at elevated temperatures. Applications: Fibremod GB306SAF has been developed especially for demanding applications in under the bonnet applications. Air intake manifolds Parts for cooling systems Fans and shrouds Technical components exposed to high heat and laods Features: Long term high heat stabilized Copper (CU) stabilized&&

Product Description
Supplier	Borealis AG
Generic	PP not specified
Material Status	Commercial: Active
Features	Chemical coupling,Copper contact stability,Heat Stabilized
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.18	g/cm³	ISO 1183
Shrinkage rate
MD：150x80x2 mm	0.10-0.20	%	ISO 294-4
TD：150x80x2 mm	0.80-1.2	%	ISO 294-4
Melt Flow Rate
230℃，2.16kg	2.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	118	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃, 50 mm/min	2.8	%	ISO 527-2
Tensile modulus
23℃，1 mm/min	9000	MPa	ISO 527-2
bending strength
23℃	170	MPa	ISO 178
Bending modulus
2 mm/min，23℃	8000	MPa	ISO 178

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed	154	℃	ISO 75-2/Af
Vicat Softening Temp
B50	142	℃	ISO 306

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength	54	kJ/m²	ISO 179/1eU
Charpy Unnotch Impact strength
23℃	58	kJ/m²	ISO 179/1eU
Charpy Notched Impact Strength	10	kJ/m²	ISO 179/1eU
Charpy Notched Impact Strength
23℃	11	kJ/m²	ISO 179/1eA
Impact strength of cantilever beam notch
23℃	11.0	kJ/m²	ISO 180-1A

Process Conditions
injection molding	Nominal value	Unit	Test method
Mold temperature	30.0-50.0	℃
Feed temperature	40.0-80.0	℃
Processing temperature	230-280	℃
Maintaining pressure	30.0-60.0	MPa
Injection speed	1667-3333	mm/s

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.