| About |
|---|
| Fibremod GB364WG is a 30% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in natural but other colours can be provided on request. This material shows excellent mechanical properties also at elevated temperatures. Applications Fibremod GB364WG has been developed especially for applications like: Pump housings Miscellaneous technical components for the white goods industry Tubs for washing machines Special Features Long term high heat stabilised UL registered under File E108112 Detergent resistant&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Chemical coupling,Heat Stabilized,Resistance to detergents |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD：2.0 mm | 1.1 | % | Internal Method |
| MD：2.0 mm | 0.20 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20 ℃, injection molding | 9.0 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20 ℃, injection molding | 49 | kJ/m² | ISO 179/1eU |
| 23 ℃, injection molding | 58 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20 ℃, injection molding | 8.5 | kJ/m² | ISO 180-1A |
| 23 ℃, injection molding | 11 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 143 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 159 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 164 | ℃ | ISO 306/A50 |
| B50 | 135 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 6900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, injection molding | 100 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, injection molding | 3.3 | % | ISO 527-2/50 |
| Bending modulus | |||
| injection molding | 6000 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 135 | MPa | ISO 178 |
| Ball hardness | |||
| H358/30 | 112 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 230 to 280 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Disk |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |