| About |
|---|
| Fibremod GD301FE is a 30 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. This material shows excellent mechanical properties also at elevated temperatures. The product is available in standard black 9502. Applications Fibremod GD301FE has been developed especially for applications like: Front end carriers Pump housings Door module carriers Pedal carriers Fans and shrouds Air bag housings&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Chemical coupling |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD：2.0 mm | 0.90 | % | Internal Method |
| MD：2.0 mm | 0.15 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2/50 |
| Bending modulus | 6500 | MPa | ISO 178 |
| bending strength | 145 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 54 | kJ/m² | ISO 179/1eU |
| 23℃ | 59 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 9.5 | kJ/m² | ISO 180-1A |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 148 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 158 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 139 | ℃ | ASTM D1525 4 |
| Melt Energy | 67.2 | kJ/kg | ISO 11357 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| atomization | |||
| 16 hr，100℃ | 1.0 | mg | DIN 75201 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| discharge | 40.0 | µgC/g | VDA 277 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 3.00 to 6.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |