| About |
|---|
| Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. 88 Shore A hardness. Processing typically conducted on standard extrusion equipment. Wire tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+TPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -40.0 | ℃ | ASTM D746 |
| Heat Deformation（100℃） | 25 | % | UL 1581 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.3E+16 | ohms·cm | ASTM D257 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 3.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Vertical Flame Test | PASSES | EN 50265-2-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 30 seconds | 88 | ASTM D2240 | |
| tensile strength | |||
| fracture | 18.0 | MPa | UL 1581 |
| fracture | 15.0 | MPa | ASTM D638 |
| Fracture, 80 ℃ | 19.0 | MPa | UL 1581 |
| fracture | 15.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 250 | % | UL 1581 |
| fracture | 220 | % | ASTM D638 |
| Fracture, 80 ℃ | 230 | % | UL 1581 |
| fracture | 220 | % | ISO 527-2/50 |
| Bending modulus | |||
| 100 mm span | 40.0 | MPa | ASTM D790 |
| — | 40.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 3. Type I, 2.0 in/min |
| 4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 6. 0.49 in/min |
| 7. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 8. UL 1581 tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |