| A low-viscosity, castable, non-shrinking urethane compound. Intended Use: Reproduce low- to medium-volume or discontinued rubber parts; form flexible molds and nonscratching holding fixtures/linings; encapsulate wire and electronics subject to impact, vibration, expansion, and contraction. Product features: Room temperature curing urethane/no heat required Mixes and pours easily 5-hour demolding time&& |
| Product Description | |
|---|---|
| Supplier | Devcon |
| Generic | PUR |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low Viscosity,Low contractility |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific volume | 0.957 | cm³/g | |
| Shrinkage rate | |||
| MD | 0.14 | % | ASTM D2566 |
| Solid content | |||
| by Volume | 100 | % | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 19.3 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 500 | % | ASTM D412 |
| tear strength | 72.7 | kN/m | ASTM D624 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 14 | kV/mm | ASTM D149 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| stripping time | 300 | min |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | 16 | hr |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 97 | ASTM D2240 | |
| Wear amount | 330 | mg/1000 cycles |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Maximum operating temperature | |||
| Dry | 82 | ℃ | |
| Wet | 49 | ℃ | |
| Thermosetting components | |||
| resin | 按重量计算的混合比: 69 | ||
| Hardening method | 按重量计算的混合比: 31 | ||
| storage stability | |||
| 24 ℃ | 10 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |