| About |
|---|
| FLEXAREN® 18001 – high quality ethylene vinyl acetate copolymer with 18% content of vinyl acetate. Manufactured by high pressure tubular process FLEXAREN® 18020 is more elastic than LDPE and compatible with a wide range of polymers. It can be processed with the same equipment.&& |
| Product Description | |
|---|---|
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Copolymer,Quick wetting |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 20℃ | 0.940 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ISO 1133 |
| Vinyl acetate content | 18.0 | wt% | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 50.0 | ℃ | ISO 306/A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Processing temperature | 100 to 150 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s A | 84 | ISO 868 | |
| Shaw’s D | 30 | ISO 868 | |
| tensile strength | ISO 527-2/1BA | ||
| fracture | 11.0 | MPa | ISO 527-2/1BA |
| 50% strain | 3.90 | MPa | ISO 527-2/1BA |
| Tensile strain | |||
| fracture | > 600 | % | ISO 527-2/1BA |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |