Flexus 7200 - SOLIAO

About
Braskem Flexus7200 is a Linear Low Density Polyethylene, metallocene ethylene-hexene copolymer, produced by gas phase process. It was specially designed to provide outstanding processing performance. Films obtained with this grade show excellent impact and puncture resistances. It contains antioxidant additives. Applications: Stretch films; liners; LDPE and HDPE blends; packages for general use. Process: Recommended processing conditions for film extrusion about 220 – 270 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.&&

About

Braskem Flexus7200 is a Linear Low Density Polyethylene, metallocene ethylene-hexene copolymer, produced by gas phase process. It was specially designed to provide outstanding processing performance. Films obtained with this grade show excellent impact and puncture resistances. It contains antioxidant additives. Applications: Stretch films; liners; LDPE and HDPE blends; packages for general use. Process: Recommended processing conditions for film extrusion about 220 – 270 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.&&

Product Description
Supplier	Braskem
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Excellent Processability,High impact resistance,Inoxidizability,Copolymer,Puncture Resistant,Hexene copolymers
Availabilitys	Latin America,Europe
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	3.5	g/10min	ASTM D1238
thickness	20.0	g/min

MECHANICAL	Nominal value	Unit	Test method
Secant modulus	180	MPa	ASTM D882
Secant modulus	190	MPa	ASTM D882
tensile strength
Fracture, thin film	40.0	MPa	ASTM D882
tensile strength
Fracture, thin film	30.0	MPa	ASTM D882
Elongation at break of thin film	990	%	ASTM D882
Elongation at break of thin film	1040	%	ASTM D882
tear strength	12.5	g/micron	ASTM D1922
tear strength	23.0	g/micron	ASTM D1922
Drop hammer impact
twenty-five μ m. Blown film	170	g	ASTM D1709

optical performance	Nominal value	Unit	Test method
Haze μ M	28	%	ASTM D1003
gloss	60	%	ASTM D2457

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.