FMC® 200 - SOLIAO

About
FMC ® -200 is a polysulfide rubber mold compound with high tear strength that cures overnight with negligible shrinkage. Molds made of FMC ® -200 are very durable and will perform in production. The mix ratio is 100 parts of Part A to 12 parts of Part B by weight. FMC ® -200 cures to a Shore hardness of 20 A. FMC ® -200 is ideal for those applications that require capturing intricate detail from a variety of model surfaces. Unlike polyurethanes, FMC ® -200 is not sensitive to moisture and can be poured directly over wet plaster or water/sulfur based clays. Common applications include molds for foundry and pattern work, sculpture (lost wax process), casting various gypsum products and waxes.&&

About

FMC ® -200 is a polysulfide rubber mold compound with high tear strength that cures overnight with negligible shrinkage. Molds made of FMC ® -200 are very durable and will perform in production. The mix ratio is 100 parts of Part A to 12 parts of Part B by weight. FMC ® -200 cures to a Shore hardness of 20 A. FMC ® -200 is ideal for those applications that require capturing intricate detail from a variety of model surfaces. Unlike polyurethanes, FMC ® -200 is not sensitive to moisture and can be poured directly over wet plaster or water/sulfur based clays. Common applications include molds for foundry and pattern work, sculpture (lost wax process), casting various gypsum products and waxes.&&

Product Description
Generic	多硫化橡胶
Material Status	Commercial: Active
Features	Low contractility,Moisture resistance,Good tear strength,Durability
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	casting

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ASTM D792
Specific volume	0.741	cm³/g

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	20		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength
fracture	1.08	MPa	ASTM D412
100% strain	0.200	MPa	ASTM D412
Tensile strain
fracture	700	%	ASTM D412

THERMAL	Nominal value	Unit	Test method
storage stability	50	min

Thermosetting mixed viscosity	Nominal value	Unit	Test method
stripping time
23℃	960	min

Supplementary information	Nominal value	Unit	Test method
Mixing ratio	100A:12B by weight

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.