| About |
|---|
| Formolene® 5102KR is a homopolymer polypropylene designed for raffia application. Its unique formulation provides excellent low water carryover. Formolene® 5102KR meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles and components of articles intended for direct food contact. This material is free of animal-derived content.&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Low water portability,Homopolymer |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.90 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze 1270 μ M | 6.2 | % | ASTM D1003 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 126 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 43 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 105 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 33.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 9.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1240 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Injection temperature | |||
| Mold temperature | 30-50 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |