| About |
|---|
| Formolene® E924F is a “low gel” high molecular weight grade of HDPE designed for high dart impact strength and good processing characteristics. Formolene® E924F is well balanced in overall physical properties and provides good stiffness for thin gauge film applications requiring high quality printing. Formolene® E924F meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Good Printability,Low speed solidification point,Food contact compliance,High molecular weight |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.040 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 8.5 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 13 | µm | |
| tensile strength | |||
| TD, fracture, 13 µ m | 28.3 | MPa | ASTM D882 |
| MD, fracture, 13 µ m | 62.1 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 13 µ m | 410 | % | ASTM D882 |
| MD, fracture, 13 µ m | 300 | % | ASTM D882 |
| Drop hammer impact | |||
| 13 µm | 210 | g | ASTM D1709 |
| tear strength | |||
| TD，13 µm | 25 | g | ASTM D1922 |
| MD，13 µm | 14 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 131 | ℃ | DSC |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. HLMI |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |