| About |
|---|
| Formolene® HB5202B2 is designed for applications requiring excellent stiffness, impact strength, and excellent stress crack resistance. It may be used as a blow molding resin or sheet extrusion thermoforming resin. Formolene® HB5202B2 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Food contact compliance,Good tear strength,High density,Hexene copolymers |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Molded into shape, F50 | 50.0 | hr | ASTM D1693B |
| 100% non-ionic detergent, molded, F50 | 50.0 | hr | ASTM D1693A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, molding | 27.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | > 600 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 1310 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -118 | ℃ | ASTM D746 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |