| Formolene® HB5502B is designed for applications requiring excellent stiffness and stress crack resistance properties. It may be used as a general-purpose blow molding resin or sheet extrusion thermoforming resin. Formolene® HB5502B meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Food contact compliance,Copolymer,Hexene copolymers,High ESCR |
| Availabilitys | North America |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.955 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.35 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Molded into shape, F50 | 35.0 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, molding | 28.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | > 600 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 1380 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -118 | ℃ | ASTM D746 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 2,0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |