| About |
|---|
| Formolene® L42009H is a general-purpose film grade linear low density made using gas-phase technology. The resin exhibits excellent toughness and strength when drawn down to thin gauges. Formolene® L42009H meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good dissection,Food contact compliance,Inoxidizability,Butylene copolymer |
| Availabilitys | North America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.95 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 28.5 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 35.2 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 920 | % | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 690 | % | ASTM D882 |
| Elmandorf tear strength | |||
| MD：25.0 µm | 57.9 | kN/m | ASTM D1922 |
| TD：25.0 µm | 148.6 | kN/m |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 42 | ASTM D523 | |
| Haze | |||
| 25 µ m, blow molded film | 18 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Drop hammer impact | |||
| 25 µm | 52.1 | kN/m | ASTM D1709 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |