| About |
|---|
| F-KVF is a medium molecular weight, fine particle PVC homopolymer dispersion which imparts pesudoplastic flow to plastisol in which it is used. Plastisol prepared utilizing F-KVF are particularly for dip, slush and rotational molding where mold release and pseudoplasticity are desired. Also fabric coating where minimum strike through is essential as well as screen printing application where fine particle and pseudoplasticity are required.&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | PVC homopolymer |
| Material Status | Commercial: Active |
| Features | Machinable,Good stripping performance,Homopolymer |
| Availabilitys | North America,Europe |
| Process Methods | Dipping coating method |
| Technical Data | |||
|---|---|---|---|
| Supplementary information | Nominal value | Unit | Test method |
| volatility | 0.50 | % | ASTM D3030 |
| Methanol extractable | 1.0 | % | ASTM D2222 |
| Gel temperature | 70 | ℃ | |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| K-Value | 67.0 | ||
| Intrinsic viscosity | 0.96 | ASTM D1243 | |
| Relative viscosity | 2.25 | ||
| Sever Viscosity | 8.00 | Pa·s | |
| Brookfield viscosity | |||
| — | 860 | Pa·s | |
| — | 92.0 | Pa·s |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 rpm, aged 2 hr |
| 3. 2 rpm, aged 2 hr |
| 4. 100 psig, aged 2 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |