| About |
|---|
| Polypropylene reinforced with nano-clay. This material has very good scratch-resistance and good impact-strength. Due to high MFI it is easy to mold. This type is designed for automotive interior/exterior trim.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High liquidity,High scratch resistance |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 7.0 | g/10min | ISO 1133 |
| Shrinkage rate | 0.80 to 1.1 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| yield | 22.0 | MPa | ISO 527-2 |
| fracture | 18.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 100 | % | ISO 527-2 |
| Bending modulus | 1200 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 49.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -20℃ | 4.5 | kJ/m² | ISO 180 |
| 23℃ | 10 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 60.0 | ℃ | ISO 306/B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 240 to 255 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |