| About |
|---|
| Glass Reinforced, Laser Direct Structuring (LDS)&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.2 | % | |
| MD | 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9500 | MPa | |
| tensile strength | |||
| fracture | 105 | MPa | |
| Tensile strain | |||
| fracture | 2.3 | % | |
| Bending modulus | 9000 | MPa | |
| bending strength | 170 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 243 | ℃ | |
| 1.8 MPa, unannealed | 213 | ℃ | |
| Melting temperature | 305 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | |
| TD | 9.0E-5 | 1/℃ | |
| Relative temperature index | |||
| Electrical performance, 0.40 mm | 65.0 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 1.00 GHz | 3.60 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.40 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 300 to 320 | °C | |
| Barrel middle temperature | 305 to 325 | °C | |
| Barrel front temperature | 310 to 325 | °C | |
| Nozzle temperature | 310 to 325 | °C | |
| Processing (melt) temperature | 310 to 330 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 0.500 to 3.00 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |