ForTii® Eco XS68

About
50% Glass Reinforced Special Features: Contains release agent Lubricated Used In: Smartphone frames ForTii® is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries. We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €” and need. That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.

About

50% Glass Reinforced Special Features: Contains release agent Lubricated Used In: Smartphone frames ForTii® is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries. We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €” and need. That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.

Product Description
Supplier	DSM
Generic	PA Not specified
Material Status	Commercial: Active
Features	Lubricating
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.56	g/cm³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	16500	MPa	ISO 527-2
tensile strength
fracture	240	MPa	ISO 527-2
Tensile strain
fracture	2.7	%	ISO 527-2
Bending modulus	15000	MPa	ISO 178
bending strength	350	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	14	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Melting temperature	305	℃	ISO 11357-3

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	100	°C
Drying time	2.0	hr
Barrel rear temperature	300 to 320	°C
Barrel middle temperature	305 to 325	°C
Barrel front temperature	310 to 325	°C
Nozzle temperature	310 to 325	°C
Processing (melt) temperature	310 to 330	°C
Mold temperature	80 to 120	°C
Injection speed	中等偏快
Back pressure	0.500 to 3.00	MPa
Screw compression ratio	2.5:1.0

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.