| A very easy flowing unfilled grade. This grade demonstrates excellent chemical resistance and thermal stability. Intended for extrusion applications that do not require high melt strength and for compounding with various fillers. Available as Fortron 0203B6 (granular powder), 0203P6 (pellets), and 0203C6 (crystallized pellets).&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good liquidity,Solvent resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 8.0 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 95.0 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 104 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 120 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 204 | ℃ | ASTM D648 |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 5.3E-5 | 1/℃ | ISO 11359-2 |
| MD | 5.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| Dielectric strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Relative permittivity | |||
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation factor | ASTM D150 | ||
| 1 MHz | 8.4E-3 | IEC 60250 | |
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 9.0E-4 | ASTM D150 | |
| Arc resistance | 124 | sec | ASTM D495 |
| Compared to the leakage tracing index | 100 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4200 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Fracture, 23 ℃ | 86.2 | MPa | ASTM D638 |
| fracture | 33.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| fracture | 1.0 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 3900 | MPa | ISO 178 |
| bending strength | 135 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 100 | ISO 2039-2 | |
| M-level | 93 | ASTM D785 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ASTM D792 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.80 to 1.0 | % | ASTM D955 |
| MD | 1.0 to 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| Specific Heat Capacity of Melt | 1830 | J/kg/℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |