| 0205 is an easy flowing unfilled grade. It demonstrates excellent chemical resistance and thermal stability. Intended for compounding with various fillers. Available standard in pellet (0205P4) and powder (0205B4) form.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good liquidity,Solvent resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 1.2 | % | ISO 294-4 |
| TD | 1.5 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.02 | % | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 115 | ℃ | ISO 75-2/Af |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | |||
| Linear coefficient of thermal expansion | |||
| MD | 5.3E-5 | 1/℃ | ISO 11359-2 |
| TD | 5.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+11 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 17 | KV/mm | IEC 60243-1 | |
| Dissipation factor | |||
| Compared to the leakage tracing index | 100 | V | IEC 60112 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.0 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 95 | M 级 | ISO 2039-2 |
| tensile strength | |||
| 23℃ | 66.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 4000 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 130 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 3900 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 -120 | °C | |
| Drying time | 3.0-4.0 | Hr | |
| Water content | 0.02 | % | |
| Injection temperature | |||
| Rear barrel temperature | 290-300 | °C | |
| Central temperature of the barrel | 300-310 | °C | |
| Barrel front temperature | 310-320 | °C | |
| Die temperature | 300-310 | °C | |
| Mold temperature | 140-160 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |