| About |
|---|
| 0214 is an unfilled grade exhibiting good melt strength. This grade demonstrates excellent heat and chemical resistance. It can be extruded to produce multi-filaments. Due to the excellent balance of flow and melt strength, this product is occasionally used for injection molding parts. Available standard in powder (0214B1), pellet (0214P1) and crystallized pellet (0214C1) form.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good liquidity,High Heat Resistance,Good melt strength,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.5 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 45 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 95.0 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 104 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 204 | ℃ | ASTM D648 |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 5.3E-5 | 1/℃ | ISO 11359-2 |
| MD | 5.2E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 3.5 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| Dielectric strength | 18 | kV/mm | IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 9.0E-4 | ASTM D150 | |
| Arc resistance | 124 | sec | ASTM D495 |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Temperature | 310 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3800 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Fracture, 23 ℃ | 86.2 | MPa | ASTM D638 |
| fracture | 90.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| fracture | 3.0 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 3750 | MPa | ISO 178 |
| bending strength | 125 | MPa | ISO 178 |
| friction coefficient | |||
| Steel – Dynamic | 0.14 | Internal Method | |
| Rockwell hardness | |||
| M-level | 93 | ASTM D785 | |
| M-level | 95 | ISO 2039-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ASTM D792 |
| Specific volume | 0.741 | cm³/g | ASTM D792 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.0 | % | ASTM D955 |
| MD | 1.2 | % | ASTM D955 |
| TD | 1.5 to 1.8 | % | ISO 294-4 |
| MD | 1.2 to 1.5 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| viscosity | 120 | Pa·s | Internal Method |
| Density of Melt | 1.150 | g/cm³ | Internal Method |
| Specific Heat Capacity of Melt | 1830 | J/kg/℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 300 to 310 | °C | |
| Barrel front temperature | 310 to 320 | °C | |
| Nozzle temperature | 300 to 310 | °C | |
| Processing (melt) temperature | 310 to 320 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection pressure | 40.0 to 80.0 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 30.0 to 60.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |