| About |
|---|
| Fortron 1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Hardness,Flame Characteristics,High Heat Resistance,Solvent resistance,Welding,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ASTM D792 |
| Specific volume | 0.636 | cm³/g | ASTM D792 |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.60 to 0.90 | % | ASTM D955 |
| MD | 0.30 to 0.50 | % | ASTM D955 |
| TD | 0.60 to 0.90 | % | ISO 294-4 |
| MD | 0.30 to 0.50 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 9.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 34 | kJ/m² | ISO 179/1eU |
| 23℃ | 34 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 9.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 30 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 266 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 280 | ℃ | ASTM D648 |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Linear coefficient of thermal expansion | |||
| TD | 5.2E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.9E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dissipation factor | ASTM D150 | ||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 1.0E-3 | ASTM D150 | |
| Arc resistance | 127 | sec | ASTM D495 |
| Compared to the leakage tracing index | 150 | V | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Specimen Thickness（Shrinkage） | 3.18 | mm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Fracture, 23 ℃ | 172 | MPa | ASTM D638 |
| fracture | 170 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.9 | % | ASTM D638 |
| fracture | 1.9 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 11000 | MPa | ISO 178 |
| bending strength | 260 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 100 | ASTM D785 | |
| M-level | 100 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 330 to 340 | °C | |
| Nozzle temperature | 310 to 330 | °C | |
| Processing (melt) temperature | 330 to 340 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection pressure | 50.0 to 100 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 30.0 to 70.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |