| About |
|---|
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Electrical performance,Good Hardness,Solvent resistance,Heat Resistance, Good,Flame Characteristics,high-rigidity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1650 | kg/m³ | ISO 1183 |
| Molding shrinkage | |||
| Parallel | 0.3 | % | ISO 294-4 |
| Normal | 0.6 | % | ISO 294-4 |
| Water Absorption | |||
| 23℃ | 0.02 | % | ISO 62 |
| Bulk density | 0.721 | g/cm³ | ISO 60 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 14700 | MPa | ISO 527 |
| Tensile Strength | |||
| Broken BRK, 5 mm/min | 195 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, 5 mm/min | 1.8 | % | ISO 527 |
| Flexural Modulus | 14500 | MPa | ISO 178 |
| Flexural Strength | |||
| Broken BRK | 285 | MPa | ISO 178 |
| Compressive modulus | 15000 | MPa | ISO 604 |
| Rockwell hardness | 100 | M Scale | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 53 | kJ/m² | ISO 179/1eU |
| -30℃ | 53 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| 23℃ | 10 | KJ/m² | ISO 180/1A |
| -30℃ | 10 | KJ/m² | ISO 180/1A |
| Izod Unnotched Impact strength of cantilever beam | |||
| 23℃ | 34 | KJ/m² | ISO 180/1U |
| -30℃ | 34 | KJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | 90 | ℃ | ISO 11357-2 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 270 | ℃ | ISO 75-1/-2 |
| 8.0 MPa | 215 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel | 0.26 | ×10-4/℃ | ISO 11359-2 |
| Normal | 0.42 | ×10-4/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Constant | 4.1 | IEC 60250 | |
| Dissipation Factor | 20 | E-4 | IEC 60250 |
| Volume Resistance | >1E13 | ohm·m | IEC 62631-3-1 |
| Surface Resistivity | 6.6E11 | ohm | IEC 62631-3-2 |
| Compared Tracking Index | 4 | PLC Code | UL 746 |
| 1500 | J/(kg K) | Internal |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen Index | 47 | % | ISO 4589-2 |
| Flame Class Rating | |||
| 1.5 mm | V-0 | calss | UL 94 |
| 0.38 mm | V-0 | calss | UL 94 |
| 3.0 mm | V-0 | calss | UL 94 |
| Glow Wire Ignitability Temperature (GWIT) | 825 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Maximum Moisture Content | 0.02 | % | |
| Drying Time | 3-4 | hr | |
| Drying Temperature | 130-140 | ℃ | |
| Hopper Temperature | 20-30 | ℃ | |
| Feeding zone temperature | 60-80 | ℃ | |
| Barrel Zone 1 Temperature | 290-300 | ℃ | |
| Barrel Zone 2 Temperature | 310-320 | ℃ | |
| Barrel Zone 3 Temperature | 330-340 | ℃ | |
| Barrel Zone 4 Temperature | 330-340 | ℃ | |
| Melt Temperature | 330 | ℃ | |
| Mold Temperature | 140-160 | ℃ | |
| Hot runner temperature | 330-340 | ℃ | |
| Back Pressure | 30 | bar | |
| Injection speed | 快速 | ||
| Screw Speed | |||
| 25 mm | 120 | rpm | |
| 40 mm | 75 | rpm | |
| 55 mm | 50 | rpm | |
| Sample thickness | 3.18 | mm | |
| Nozzle temperature | 310-330 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |