| About |
|---|
| Fortron 1140L6FC is an easier flow version of Fortron 1140L4 made for food contact applications. It offers essentially the same characteristics of 1140L4. Especially used for thin walled parts with long flow lengths. Applications made of this grade include components for pumps and electronics.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Negative |
| Features | Good liquidity,Food contact compliance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 53 | kJ/m² | ISO 179/1eU |
| 23℃ | 53 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 34 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 280 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 265 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 270 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 215 | ℃ | ISO 75-2/C |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 2.6E-5 | 1/℃ | ISO 11359-2 |
| TD | 4.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | |||
| — | 1.0E+16 | ohms·cm | ASTM D257 |
| — | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| — | 15 | kV/mm | ASTM D149 |
| — | 28 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 kHz | 3.50 | ASTM D150 | |
| 1 MHz | 3.50 | ASTM D150 | |
| 1 MHz | 4.20 | IEC 60250 | |
| Dissipation factor | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | IEC 60250 | |
| Arc resistance | 134 | sec | ASTM D495 |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.38 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| CSA Rating（840.0 µm） | A00 | CSA F-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 100 | ASTM D785 | |
| M-level | 100 | ISO 2039-2 | |
| Tensile modulus | 14700 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Fracture, 23 ℃ | 200 | MPa | ASTM D638 |
| fracture | 195 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ASTM D638 |
| fracture | 1.9 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 14500 | MPa | ISO 178 |
| bending strength | 285 | MPa | ISO 178 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| — | 1.60 | g/cm³ | ASTM D792 |
| — | 1.65 | g/cm³ | ISO 1183 |
| Specific volume | 0.625 | cm³/g | ASTM D792 |
| Melt Flow Rate | 19 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.30 | % | ASTM D955 |
| TD | 0.50 to 0.70 | % | ASTM D955 |
| TD | 0.40 to 0.60 | % | ISO 294-4 |
| MD | 0.20 to 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| Spiral flow length | 21.5 | Internal Method | |
| Specific Heat Capacity of Melt | 1500 | J/kg/℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 330 to 340 | °C | |
| Nozzle temperature | 310 to 330 | °C | |
| Processing (melt) temperature | 330 to 340 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection pressure | 50.0 to 100 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |