| About |
|---|
| Fortron 1200L1 is an unfilled grade recommended primarily for extrusion applications. It has a high melt viscosity and tensile elongation. Recommended processing conditions are similar to those of our standard unfilled PPS grades.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | High Viscosity,Good Tensile Strength |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| viscosity | 430 | Pa·s | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 200 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 275 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 4.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 4.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 10 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 93 | ISO 2039-2 | |
| Tensile modulus | 4000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 88.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | ISO 527-2/1A/50 | ||
| yield | 3.0 | % | ISO 527-2/1A/50 |
| fracture | 15 | % | ISO 527-2/1A/50 |
| Bending modulus | |||
| 23℃ | 4100 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 141 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |