| About |
|---|
| Fortron 6165A6FC is an easier flow version of Fortron 6165A4 for use in food contact applications. It offers similar characteristics to the 6165A4.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good liquidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | |||
| -30℃ | 7.0 | kJ/m² | |
| 23℃ | 7.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 20 | kJ/m² | |
| 23℃ | 20 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 270 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 215 | ℃ | ISO 75-2/C |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.9E-5 | 1/℃ | |
| TD | 2.4E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 25 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 5.60 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 2.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | ||
| 1.50 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 100 | ISO 2039-2 | |
| Tensile modulus | 19000 | MPa | ISO 527-2/1A |
| tensile strength | |||
| fracture | 130 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.2 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 18800 | MPa | ISO 178 |
| bending strength | 210 | MPa | ISO 178 |
| Compression modulus | 18500 | MPa | ISO 604 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.95 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.30 to 0.70 | % | |
| MD | 0.20 to 0.60 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| Specific Heat Capacity of Melt | 1600 | J/kg/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 330 to 340 | °C | |
| Nozzle temperature | 310 to 330 | °C | |
| Processing (melt) temperature | 330 to 340 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection speed | 快速 | ||
| Back pressure | < 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |