| About |
|---|
| Fortron 6450A6 is a fiberglass reinforced, mineral filled alloy that exhibits improved wear and sliding properties versus standard Fortron compounds.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Good wear resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 90.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.5 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 11000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 130 | MPa | ISO 178 |
| friction coefficient | ASTM D1894 | ||
| dynamic | 0.31 | ASTM D1894 | |
| dynamic | 0.34 | ASTM D1894 | |
| static state | 0.37 | ASTM D1894 | |
| static state | 0.31 | ASTM D1894 | |
| Steel – Dynamic | 0.13 | ASTM D1894 | |
| vs. Steel – Static 4 | 0.16 | ASTM D1894 | |
| Wear factor | ASTM D3702 | ||
| 416 Stainless：32℃ | 164 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel：49℃ | 217 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel：93℃ | 300 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 18 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 200 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 260 | ℃ | ISO 75-2/A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 330 to 340 | °C | |
| Nozzle temperature | 310 to 330 | °C | |
| Processing (melt) temperature | 330 to 340 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection pressure | 50.0 to 100 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 30.0 to 70.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |