| About |
|---|
| Fortron® FX32T4 is an unreinforced, impact-modified poly(phenylene sulfide) with high flowability suitable for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Negative |
| Features | High impact resistance,High liquidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.2 | % | ISO 294-4 |
| MD | 1.2 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 50.0 | MPa | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 20 | % | ISO 527-2/1A/50 |
| Bending modulus | |||
| 23℃ | 2300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 158 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 6.9E-5 | 1/℃ | ISO 11359-2 |
| TD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+17 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1 MHz | 3.35 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 2.0E-4 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 280 to 300 | °C | |
| Barrel middle temperature | 285 to 305 | °C | |
| Barrel front temperature | 285 to 305 | °C | |
| Nozzle temperature | 290 to 320 | °C | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |