| About |
|---|
| FORTRON® MT9140L6 SF3001 (natural) is a 40% glass fiber reinforced injection molding grade with a low melt viscosity. FORTRON® MT9140L6 SF3001 (natural) is a special grade developed for medical industry applications and complies with: Food Contact Substance Notification (FCN) No. 40 of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 14844) and the Device Master File (MAF 1097) the corresponding EU and national registry regulatory requirements biocompatibility in tests corresponding to USP 23 Class VI/ISO 10993 low residual monomers no animal products It exhibits excellent heat and chemical resistance, inherent flame retardancy and shows high hardness and rigidity at elevated temperatures. Fortron MT9140L6 is used for thin walled parts with long flow lengths. Components made of this grade may be used for medical, dental, pharmaceutical, and certain food handling applications.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low Viscosity,Good Hardness,Flame Characteristics,Food contact compliance,High Heat Resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.40 to 0.60 | % | ISO 294-4 |
| MD | 0.20 to 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 48 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 32 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 200 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 270 | ℃ | ISO 75-2/A |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 190 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.8 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 14000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 280 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 100 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 330 to 340 | °C | |
| Nozzle temperature | 310 to 330 | °C | |
| Processing (melt) temperature | 330 to 340 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection pressure | 50.0 to 100 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 30.0 to 70.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |